CHARACTERISTICS
Expafol presents the newest generation of clear PVC films made with the latest and most modern technology. Low Shink window films solve fundamental problems of textile architecture industry:
LOW SHRINK AVOIDS ALMOST COMPLETELY THERMODYNAMIC SHRINKAGE OF PVC FILM WHEN EXPOSED TO HIGH TEMPERATURES.
Low Shrink window film is especially recommended for climates with hot summers. It is advised for large-scale tents, enclosures with big windows, structures with zipper closures and textile architecture.
Thickness 500/630 micron in width 137 cm and 30 m roll length.
Thickness |
Quality |
Width |
Roll |
Weight roll |
|---|---|---|---|---|
500 μm |
Uv Ht |
137 cm |
30 m |
28 kg |
650 μm |
Uv Ht |
137 cm |
30 m |
36 kg |
Characteristics |
Value |
Test method |
|---|---|---|
Composition |
PVC |
|
Thickness |
500 μm 650 μm |
ASTM D-792 |
Tensile strength |
L: 220 Kg/cm² T: 210 Kg/cm² |
ASTM D-882 |
Elongation at break |
L: 380 % T: 420 % |
ASTM D-882 |
Temperature resistance |
-10 ºC / +70 ºC |
DIN EN 1876-1 |
Shrinkage average |
<1% |
24 h - 60 ºC |
Ultraviolet Resistance |
Blue scale > 5 |
EN ISO 105 B2 |
Flame retardancy standard |
— |
UNE 23727-90 |
Electrical resistivity |
— |
JIS K-6911 20ºC 60% RH |
Volume resistivity |
— |
— |
Static decay time |
— |
MIL B-81705D Static Decay Meter |